| 稀土Y对Fe71.4Si13B9.6Mo2Cr1Cu1P2合金晶化行为及磁性能的影响 |
| Effects of rare-earth yttrium on crystallization and magnetic properties of Fe71.4Si13B9.6Mo2Cr1Cu1P2 nanocrystalline alloy |
| 投稿时间：2016-11-03 |
| DOI： |
| 中文关键词: 铁基非晶合金 稀土Y 晶化行为 磁性能 |
| 英文关键词: Fe-based amorphous alloy rare earth element Y crystallization property magnetic property |
| 基金项目:国家自然科学基金资助项目(11574242). |
| 作者 | 单位 | E-mail | | 戴明杰 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | daimingjie_wh@163.com | | 徐黎明 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | | | 周欢华 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | | | 甘章华 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | | | 卢志红 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | | | 刘静 | 武汉科技大学省部共建耐火材料与冶金国家重点实验室,湖北 武汉,430081 | |
|
| 摘要点击次数: 6513 |
| 全文下载次数: 2974 |
| 中文摘要: |
| 采用单辊甩带法,在大气环境下制备Fe71.4-ySi13B9.6Mo2Cr1Cu1P2Yy (y=0、0.0050、0.0077)合金条带,并将其绕制成环状铁芯,利用差热分析法、HT35铁芯测量仪和软磁性能测量仪等手段,分析添加微量稀土元素Y对Fe71.4Si13B9.6Mo2Cr1Cu1P2合金晶化行为及磁性能的影响。结果表明,随着稀土元素Y含量的增加,合金条带的初始晶化温度逐渐降低,与没有添加稀土元素Y的试样相比,其最佳退火温度降低5~10 ℃；添加稀土元素Y可提高合金的磁导率和磁感应强度,其中,当y=0.0077时,所制合金的最大磁导率为5.5×105 Gs/Oe,饱和磁感应强度达到1.192 T；所制合金的矫顽力和损耗随稀土元素Y含量的增加均有所增大。 |
| 英文摘要: |
| Fe71.4-ySi13B9.6Mo2Cr1Cu1P2Yy (y=0、0.0050、0.0077) amorphous alloy ribbons were prepared by a single-roller melt spinner in atmospheric environment. The effects of Y addition on the crystallization and magnetic properties of the Fe71.4Si13B9.6Mo2Cr1Cu1P2 alloy were studied by differential thermal analysis,HT35 core measuring instrument and soft magnetic property measurement instrument. The results show that with increasing content of Y, the initial crystallization temperature decreases .Compared with the sample without Y addition, the best annealing temperature decreases by about 5~10 ℃. The addition of Y can improve the maximum permeability and saturation magnetic induction intensity of the alloy. When y=0.0077, the maximum permeability of the alloy is 5.5×105 Gs/Oe and the saturation magnetic induction intensity of the alloy can reach 1.192 T. However, coercive force and core loss of the alloy both see a slight increase. |
|